Two-component, solvent-free, epoxy-based transparent coating material
A solvent-free, epoxy-based transparent coating material. It is a coating with good penetration properties, resistance to chemicals and high mechanical strength.
Πεδία Χρήσης
- Shopping centres
- Schools, hospitals, the pharmaceutical sector, the food sector
- Laboratories
- In car parks, shops and similar areas
- Can be applied in 3D applications, on its own as a varnish, or with decorative coloured quartz as a terrazzo coating
Πλεονεκτήματα
- Durable and long-lasting
- Excellent final-coating performance
- Excellent abrasion and chemical resistance.
- A thick-build coating with easy application.
- Good adhesion to epoxy primers and polyurethane coatings (provides an excellent topcoat)
- Fast curing, hygienic and easy to clean.
- Can be applied indoors and outdoors.
Συσκευασίες & Προσφορά
16 kg + 4 kg set
Εισαγάγετε ποσότητα για το μέγεθος συσκευασίας που χρειάζεστε και προσθέστε το στη λίστα προσφοράς σας, ώστε το αίτημά σας να δηλώνει εξαρχής την ακριβή συσκευασία.
| Συσκευασία | Ποσ. | |
|---|---|---|
| 16 kg + 4 kg set |
| Κατανάλωση | Total theoretical consumption: 1.60 kg/m² per 1 mm thickness |
|---|---|
| Διάρκεια Ζωής | Can be stored for 6 months in its unopened original packaging in a dry environment at temperatures between 5°C and 25°C. Opened packages must be used immediately. |
Εφαρμογή
Weak sections of the surfaces to be coated must be removed by milling, sand blasting or sanding. If the surface is very smooth, it should likewise be roughened by milling or sand blasting to increase the specific surface area. Any oil on the surface must be burned off, and dirt and dust removed by vacuum. After a primer has been applied to the cleaned surfaces, the solvent-free transparent epoxy coating is spread over the surface with a notched trowel at the consumption rate appropriate to the desired thickness. Gas bubbles are carefully popped with the aid of a torch and the coating is left to cure. Application tools: roller or brush.
Τεχνικά Χαρακτηριστικά
| KOMPONENT SAYISI | 2 |
|---|---|
| YOĞUNLUK (KARIŞIM) | 1,00 - 1,10 gr/cm³ 20°C (TS EN ISO 2811-1) |
| VİSKOZİTE | 300-500 mPas |
| KATI MADDE KARIŞIM (%) | Ağırlıkça 100, Hacimce 100 |
| UYGULAMA TİNERİ | İnceltilmez |
| KARIŞIM ORANI | A/B: 68/32; 80/20 (Ağırlıkça) |
| KARIŞIM ÖMRÜ | 30-40 Dakika / 23°C, 200 g. (DIN 16945) |
| UYGULAMA ŞEKLİ | Rulo, Fırça |
| SARFİYAT | Yüzeye bağlı olarak 1mm kalınlık için 1m²’de 1,1 kg |
| KURUMA SÜRESİ — Toz Kuruma | 3-4 saat 23°C (TS 4317) |
| KURUMA SÜRESİ — Dokunma Kuruması | 8-10 saat 23°C (TS 4317) |
| KURUMA SÜRESİ — Tam Kuruma | 7 gün 23°C (TS 4317) |
| ÇEKME DAYANIMI (N/mm²) | 20 ~ 24 (DIN 53504 TS 1967) |
| ÇEKME UZAMASI (%) | 1,8 - 2,0 (DIN 53504 TS 1967) |
| E-MODÜL (N/mm²) | 20 ~ 24 (DIN 52371 TS 985) |
| EĞİLME DAYANIMI (N/mm²) | 0,5 (DIN 52371 TS 985) |
| Kimyasal Dayanım — Sülfirik Asit (H₂SO₄) %10 | 3-2 |
| Kimyasal Dayanım — Sülfirik Asit (H₂SO₄) %20 | 3-2 |
| Kimyasal Dayanım — Hidroklorik Asit (HCL) %10 | 3-2 |
| Kimyasal Dayanım — Hidroklorik Asit (HCL) %20 | 3-2 |
| Kimyasal Dayanım — Nitrik Asit (HNO₃) %10 | 3-2 |
| Kimyasal Dayanım — Nitrik Asit (HNO₃) %20 | 3-2 |
| Kimyasal Dayanım — Asetik Asit (CH₃COOH) %10 | 3-2 |
| Kimyasal Dayanım — Asetik Asit (CH₃COOH) %20 | 2 |
| Kimyasal Dayanım — Laktik Asit (CH₃CHOH) %10 | 2 |
| Kimyasal Dayanım — Laktik Asit (CH₃CHOH) %20 | 2-1 |
| Kimyasal Dayanım — Formik Asit (HCOOH) %10 | 2 |
| Kimyasal Dayanım — Formik Asit (HCOOH) %20 | 2-1 |
| Kimyasal Dayanım — Kesilen | 2 |
| Kimyasal Dayanım — Etil Alkol | 2 |
| Kimyasal Dayanım — Solventler | 2 |
| Kimyasal Dayanım — Kromik Asit (H₂CRO₄) %10 | 2 |
| Kimyasal Dayanım — Sodyum Hidroklit (NaOH) | 3 |
| Kimyasal Dayanım — Değerlendirme | 3: Çok Dayanıklı, 2: Dayanıklı, 1: Dayanıksız |