EPOXY TX

Solvent-free, orange-peel effect epoxy topcoat

A solvent-free epoxy paint; a two-component thixotropic epoxy coating. High surface hardness, water and chemical resistance, high mechanical resistance and easy cleaning are its distinguishing properties.

Πεδία Χρήσης

• Factories
• Warehouses
• Shopping centres
• Workshops
• Aircraft hangars
• Schools
• Hospitals
• The pharmaceutical sector
• The food sector
• Laboratories
• Car parks
• Treatment plants
• As a topcoat on metal or concrete in areas subject to heavy forklift traffic and corrosive chemicals.

Πλεονεκτήματα

• Has high surface hardness.
• High resistance to chemicals.
• High mechanical resistance.
• Easy to clean.

Κατανάλωση	550 g/m² (300 µ dry film thickness)

Εφαρμογή

Surfaces to be coated must not contain defects such as pits, breaks, segregation or cracks, and must not be dusting. Such defects must be corrected before application with TERAPOL EPOXY REPAIR (epoxy-based repair mortar). Surface preparation must be carried out by shot blasting, milling, sanding or similar mechanical surface-abrasion methods, and all surfaces must be de-dusted with industrial vacuum equipment. Under all conditions, surface adhesion must be above 1.5 N/mm² and the moisture content below 4%. During application, care must be taken that the floor temperature is at least +3°C above the dew point. Preparing and applying the primer: where a primer is required, TERAPOL EPOXY PRIMER is used. The primer is applied in a single coat by roller. Consumption is approximately 0.30-0.50 kg/m². Preparing the mix: components A and B are mixed with a low-speed mixer (below 400 rpm) and a mixing paddle until a homogeneous consistency is reached. Applying EPOXY TX: the mix is spread over the surface in a homogeneous thickness with a fine-notched trowel or roller, and a crystal-patterned sponge roller is then passed over it to obtain a textured coating. Always working with the pattern roller in the same direction and in a regular manner is important for achieving a flawless result.

Τεχνικά Χαρακτηριστικά

Parlaklık	Parlak
Yoğunluk	1,70-1,90 gr/cm³ (TS EN ISO 2811-1)
Viskozite	5,4-5,9 tix index
Katı Madde Karışım (%)	Ağırlıkça 100, Hacimce 100
Uygulama Tineri	İnceltilmez
Karışım Oranı	Ağırlıkça: A/B: 90/10
Karışım Ömrü	40-60 dak. / 23˚C, 200 g. (DIN 16945)
Kuruma Süresi — Toz Kuruma	60-90 dk. 23°C (TS 4317)
Kuruma Süresi — Dokunma Kuruması	6-8 saat 23°C (TS 4317)
Kuruma Süresi — Kat Kabul	24 saat 23°C (TS 4317)
Kuruma Süresi — Tam Kuruma	7 gün 23°C (TS 4317)
Aşınma Direnci (Taber)	115 mg 1000 devir (EN 1504-2)
Çekip koparma yoluyla yapışma dayanımı	>2,0 (1,5)b (EN 1504-2)
Çarpmaya Direnç deneyi	Sınıf III (EN 1504-2)
Kapilar su emme ve su geçirgenliği	<0,1 kg/m². h0,5 (EN 1504-2)
Shore D	80±5 (ASTM D 2240, DIN 53505)
Basınç Dayanımı (N/mm²)	55 ~ 57 (DIN 53504 TS 1967)