POLYUREA-S

Two-component, flexible, highly reactive pure polyurea spray coating material

Polyurea-S is a two-component, flexible, highly reactive pure polyurea spray coating material formed by the reaction of an isocyanate-based prepolymer with a multifunctional polyamine blend.

Πεδία Χρήσης

• Roofs
• Terraces
• Industrial surfaces
• Roads
• Car parks
• Pipes
• Commercial vehicle coatings
• Pools

Πλεονεκτήματα

• Fast curing
• Seamless application, including on vertical surfaces
• High mechanical strength
• Chemical resistance
• Corrosion resistance
• Abrasion resistance
• Environmentally friendly (contains no VOCs)

Κατανάλωση	1.1-1.2 kg/m² for a 1 mm thick polyurea coating

Εφαρμογή

Before application, oil, grease, paraffin residues, cement laitance, loose particles, form-release agents, cured old membranes and similar factors that would weaken adhesion must be removed from all surfaces. If possible, the surface should be cleaned by washing with high-pressure water and then dried; surface defects should be repaired with TP REPAIR-800 cement-based repair mortar. The moisture content of the concrete must be checked; the maximum moisture content is 4%. At the start, the spray application may be very soft or hard depending on the substrate temperature. The product begins to gain strength after 1-2 hours, reaches 95% of its strength values after one day, and its full values after one week. After the levelling work, EPOXY PRIMER should be used. It must be applied with spray equipment capable of operating at high pressure and temperature, in order to mix the polyamine component homogeneously with the isocyanate prepolymer and spray it. CONCRETE FLOORS: a) First, the mechanical preparations are carried out. 1- Large damaged areas are filled with concrete (on old floors) 2- Large cracks in the floor are cross-cut with a diamond saw and reinforced with steel elements at 40 cm intervals 3- The floor must be clean and free of oils. b) POLYUREA-S waterproofing is applied. Asphalt, concrete and similar materials can be applied on top of it. POLYUREA-S AS A TOP COAT: Applied on new buildings and during reconstruction — for example over old industrial floors, on roofs, walls, pools and parking areas. The final coat is slightly textured. Quartz can be broadcast over it to make it non-slip (to increase slip resistance). The desired topcoat colour can be achieved by applying aliphatic PUR TOP COAT-C. Application tools: high-pressure compressor (pneumatic/hydraulic) (min. 7 bar).

Τεχνικά Χαρακτηριστικά

Yoğunluk (25°C)	A: 1,10 - 1,12 / B: 1,00 - 1,05 g/cm³ (ASTM D 4052)
Viskozite (25°C)	A: 500 - 750 / B: 600 - 750 cP (ASTM D 4878)
Toplam Katı Madde Miktarı	A: %100 / B: %100 (İç metod)
Jelleşme Zamanı	5 - 7 sn (İç metod)
Ele Yapışmama Zamanı	13 - 20 sn (İç metod)
Sertlik	Shore A 80 - 95 (DIN 53505)
Yırtılma Direnci	35 - 45 N/mm (ASTM D 624)
Uzama	%525 - 600 (ASTM D 412)
Kopma Mukavemeti	14 - 17 N/mm² (ASTM D 412)
Karışım oranı (Prepolimer/poliamin)	Ağırlıkça 100 / 100, Hacimce 100 / 100
Uygulama Sıcaklığı	70 - 80 °C
Uygulama Basıncı	120 - 200 bar